COLLOY A-Z-N 200 能够生成一种均匀，镜面光亮，柔韧性好的含镍量为8%-16%锌镍合金层，并能在低、中、高电流密度区均匀分布。
COLLOY A-Z-N 200 可在32°-42°C温度下操作，镀液温度低，使用经济节省。
COLLOY A-Z-N 200 给予恰当钝化后，合金镀层能提供比镀锌层更高的耐盐雾能力。
COLLOY A-Z-N 200 此工艺适用于可锻铸铁、热处理或其它加硬的钢铁工件基材上。
COLLOY A-Z-N 200 无需硼酸。
COLLOY A-Z-N 200 操作范围广，使用简便。
COLLOY A-Z-N 200 此工艺不需要为锌镍的溶解分别使用单独的整流器。
COLLOY A-Z-N 200 镀层适用于三价铬蓝色、彩色和黑色钝化，也适用于其他六价铬工艺钝化。
Performance advantages
COLLOY A-Z-N 200 for ammonium chloride zinc/nickle alloy plating process
Irovides a level, mirror bright, ductile electro-deposited zinc-nickel alloy containing from 8% to 16% nickel that is evenly distributed at low, mid and high current densities.
Operates at lower, more economical temperatures of 90° - 110°F (32° - 42°C).
The deposits provide greatly enhanced corrosion resistance compared to zinc plate when properly chromated.
The bath readily plate substrates such as malleable iron castings, heat treated and other hardened steels.
Does not require Boric Acid.
It has a wide operating range and user friendly Brightener-Carrier system.
The process does not require separate rectifiers.
The deposits accept Trivalent